FINGERPRINTING PROPERTIES
HDPE GEOMEMBRANE (Made from Chevron PHILLIPS
Resin)
|
| |
| Density (ASTM D1505) - |
|
.938 gm/ cc (resin)
.947 gm/ cc (sheet) minimum 0.940 |
| |
| Melt Index (ASTM D1238) - |
|
.11 gm/ 10 min (resin)
.15 gm/ 10 min (sheet) maximum 0.4 gm/10 min |
| |
| High Load Melt Index Ratio - |
|
110 (resin)
|
| |
| Carbon Black (ASTM D1603) - |
|
Typical- 2.4% (sheet)
Minimum 2% |
| |
| DSC Melt Point - |
|
126 deg C.
.15 gm/ 10 min (sheet) minimum |
| |
|
| Note: Resin is natural (wo/
carbon black) |
| |
| |
 |
 |